RAPID FUSE
1630
Rapid FUSE 1630 is a polyethylene based
free-flowing powder. The key characteristic of this powder is its
low melting temperature. Low melting temperature helps to
increase line speeds and lower energy costs.
POLYMERS
All
powders are manufactured from prime virgin grades of polymers
manufactured by the major polymer producers. All the grades
mentioned have been manufactured from polymers that meet the
requirements to Indian Standard IS:10146-1982 on "Polyethylene for
its safe use in contact with foodstuffs, pharmaceuticals and drinking
water"
Technical
Specifications
(Data shown are average values and
should not be used for specification
results)
|
PROPERTY
|
TEST
METHOD
|
VALUE
|
|
Material
|
Prime Virgin
Grade
|
Polyethylene
|
|
Specific
Gravity
|
ASTM
D1505
|
0.918 gms./
cc
|
|
Vicat
Softening Point
|
ASTM
D1525
|
84°C
|
|
Melt Indix
190°C/I2.16
|
ASTM
D1238
|
~30 gms./ 10
min
|
|
Tensile
Strength at Yield
|
ASTM
D638
|
90 kg/
cm2
|
|
Elongation at
Yield
|
ASTM
D638
|
700%
|
|
Flexural
Modulus
|
ASTM
D790
|
1,400 kg/
cm2
|
|
Powder
Particle Size
|
|
Finer than
300µm
|
|
Coverage
|
100%
efficiency
|
3.1
m2/ kg.@350mm
|
|
Taber
Abrasion
|
ASTM
D4060
|
30 mg.Weight
loss
|
|
QUV
|
ASTM
D2244
|
0.5ÑE
|
|
Colors
|
|
Black and
Natural available
ex-stock
|
TYPICAL
APPLICATIONS
Fusible Interlining Fabric for
garments and textiles.
|
The data, information and
suggestions provide here are to the best of our knowledge true and
accurate. Rapid Engineering Co. Pvt. Ltd. undertakes no
responsibility either for the result deriving from their adoption or
for possible positions in apparent contrast with existing patent
rights.
|
|
|